FeOOH/MnO2吸附水体中砷的性能研究

FeOOH/MnO2吸附水体中砷的性能研究(5800字)
摘  要：为了增加材料对水体中砷的吸附性能，本论文利用化学沉积法在纳米MnO2表面修饰了不同量的FeOOH获得了四种FeOOH/MnO2材料。通过对比筛选出20/100的FeOOH/MnO2材料具有最高的吸附容量，研究了pH、砷浓度、时间、温度对20/100的FeOOH/ MnO2吸附水中砷的影响。结果表明，20/100的FeOOH/MnO2对砷的吸附最适pH为6、吸附容量为19.7mg/g、平衡吸附时间为30min，但是温度对吸附情况几乎没影响。
关键词：铁锰氧化物；砷；吸附

the FeOOH/ MnO2 removal of arsenic form water
Abstract: In order to increase the adsorption performance of arsenic in the water. This study made 4 types of FeOOH/ MnO2, After chosen the best material, I made a analysis of the influence of pH, arsenic concentration, time and temperature on effect of the absorption of arsenic from water by 20/100 FeOOH/ MnO2. The results showed that arsenic could be adsorbed efficiently by 20/100 FeOOH/ MnO2 at pH = 6 and after 30min, the adsorption capacities for arsenic was 19.7 mg•g- 1, but temperature almost without effect.

[来源：http://www.think58.com]

Key Words: FeOOH/ MnO2 Arsenic water Absorption   

目录
摘  要    1
1    前言    1
2    材料仪器    3
2.1    试剂    3
2.2    仪器    3
3    试验方法    3
3.1    FeOOH/ MnO2的制备与表征    3
3.2    砷溶液的配置及吸附实验    4
3.3    吸附容量最大材料的筛选    4
3.4    pH对20/100 的FeOOH/ MnO2吸附As的影响    4
3.5    20/100 的FeOOH/ MnO2对不同浓度As的吸附容量    4
3.6    时间对20/100 的FeOOH/ MnO2吸附As的影响    4
3.7    温度对20/100 的FeOOH/ MnO2吸附As的影响    4
4    结果与讨论    5
4.1    各种材料的XRD图    5
4.2    选出吸附容量最大的材料    5
4.3    pH对20/100的FeOOH/ MnO2吸附As的影响    6
4.4    20/100 的FeOOH/ MnO2对不同浓度As的吸附容量    6
4.5    时间对20/100 的FeOOH/ MnO2吸附As的影响    7
4.6    温度对20/100 的FeOOH/ MnO2吸附As的影响    7
4.7    红外分析    8
5    结论    8
参考文献    8
致    谢    10

[资料来源：http://THINK58.com]